Expansion Fabric Joint
Suntex offers a variety of materials for manufacturing expansion fabric joints, which are widely used in industries such as power plants, cement factories, and chemical plants.

Expansion fabric joints require different types of fabrics for various components, and Suntex can supply most of these materials as below.


Silicone coated fiberglass fabric
Silicone-coated fiberglass fabric is ideal for expansion joints due to its high-temperature resistance, flexibility, durability, and excellent weather and chemical resistance, ensuring long-lasting performance.

Style No. | Weight | Thickness | Color | Coating |
---|---|---|---|---|
Suntex-1260 | 530gsm | 0.4mm | grey | 2 sides |
Suntex-1320 | 630gsm | 0.45mm | black | 2 sides |
Suntex-1022 | 960gsm | 0.7mm | red | 2 sides |
Suntex-1023 | 960gsm | 0.7mm | black | 1 side |
Suntex-1236 | 960gsm | 0.7mm | grey | 1 side |
Suntex-1027 | 1120gsm | 0.9mm | grey | 2 sides |
Suntex-1270 | 1640gsm | 1.0mm | black | 1 side |
Suntex-1208 | 1380gsm | 1.2mm | red | 1 side |
Silicone coated aramid fabric
Silicone-coated aramid fabric is suitable for expansion joints due to its high strength, heat resistance, flexibility, and durability, along with excellent chemical and abrasion resistance for demanding environments.

Style No. | Weight | Thickness | Color | Coating |
---|---|---|---|---|
Suntex-1185 | 490gsm | 0.5mm | grey | 1 side |
Suntex-1304 | 690gsm | 0.6mm | red | 2 sides |
Suntex-1283 | 1650gsm | 1.5mm | black | 2 sides |
Neoprene coated fiberglass fabric
Neoprene coated aramid fabric is ideal for expansion joints due to its excellent abrasion resistance, flexibility, weather resistance, and ability to withstand a range of temperatures and chemicals, ensuring durability.

Style No. | Weight | Thickness | Color | Coating |
---|---|---|---|---|
Suntex-4004 | 800gsm | 0.55mm | black | 2 sides |
Hypalon coated fabric
Hypalon coated fabric is suitable for expansion joints due to its exceptional chemical resistance, UV stability, flexibility, and durability, making it ideal for harsh environments and extreme temperatures.
Style No. | Basic fabric | Weight | Thickness | Color | Coating |
---|---|---|---|---|---|
Suntex-8022 | polyester fabric | 1200gsm | 1.0mm | grey | 2 sides |
Suntex-8025 | fiberglass fabric | 420gsm | 0.3mm | grey | 2 sides |
Fluoroelastomer coated fabric
Fluoroelastomer coated fabric is ideal for expansion joints due to its outstanding chemical resistance, high-temperature stability, and durability, ensuring reliable performance in harsh and demanding environments.
Style No. | Basic fabric | Weight | Thickness | Color | Coating |
---|---|---|---|---|---|
Suntex-8027 | aramid fabric | 160gsm | 0.3mm | white | 1 side |
PTFE coated fiberglass fabric
PTFE-coated fiberglass fabric is ideal for expansion joints due to its excellent chemical resistance, high-temperature stability, low friction, and durability, ensuring reliable performance in harsh industrial environments.


Style No. | Weight | Thickness | Color | Coating |
---|---|---|---|---|
Suntex-8001 | 580gsm | 0.4mm | black | 1 side |
Suntex-8003 | 580gsm | 0.4mm | grey | 1 side |
Suntex-8018 | 610gsm | 0.4mm | black | 2 sides |
Suntex-8019 | 1300gsm | 1.0mm | black | 2 sides |
Alumimum foil/film coated fiberglass fabric
Aluminum-coated fiberglass fabric is suitable for expansion joints due to its reflective properties, high-temperature resistance, and durability, providing thermal insulation and protection in extreme environments.

Style No. | Weight | Thickness | Color | Coating |
---|---|---|---|---|
Suntex-6008 | 450gsm | 0.4mm | sliver | 1 side |
High temperature fiberglass fabric
High-temperature fiberglass fabric is ideal for expansion joints due to its ability to withstand extreme heat, excellent tensile strength, durability, and resistance to chemical exposure, ensuring reliable performance.

Style No. | Basic fabric | Weight | Thickness | Color | Coating |
---|---|---|---|---|---|
Suntex-2017 | fiberglass fabric | 690gsm | 0.6mm | grey | 1 side |
Suntex-2019 | fiberglass fabric | 620gsm | 0.75mm | grey | 2 sides |
Suntex-2061 | fiberglass fabric | 1050gsm | 1.0mm | grey | 2 sides |
Suntex-2056 | fiberglass fabric | 1100gsm | 1.2mm | black | 2 sides |
Suntex-2025 | fiberglass fabric | 1070gsm | 1.2mm | green | 1 side |
Suntex-5002 | fiberglass fabric | 1100gsm | 1.2mm | black | 2 sides graphite |
Suntex-5006 | fiberglass fabric | 1100gsm | 1.2mm | grey | 2 sides high temp |
SL600 | silica fabric | 600gsm | 0.65mm | white | N/A |
SL1100 | silica fabric | 1100gsm | 1.2mm | white | N/A |
Suntex-5021 | silica fabric | 620gsm | 0.65mm | yellow | 2 sides vermiculite |
Suntex-5022 | silica fabric | 1250gsm | 1.25mm | yellow | 2 sides vermiculite |
High temperature fiberglass fabric with S.S wire reinforced
High-temperature fiberglass fabric reinforced with stainless steel wire offers enhanced strength, durability, and resistance to deformation under stress, making it ideal for expansion joints in extreme conditions.


Style No. | Basic fabric | Weight | Thickness | Color | Coating |
---|---|---|---|---|---|
Suntex-5058 | ECR | 1230gsm | 1.3mm | grey | 2 sides high temp |
Suntex-5065 | ECR | 1250gsm | 1.3mm | yellow | 2 sides vermiculite |